Test specimens were austenitised and experienced large amounts of decarburisation (loss of carbon) and scaling. / Toetsmonsters is geaustenitiseerd en het groot hoeveelhede ontkoling (verlies aan koolstof) en skaal ervaar.

The fully austenitised test specimen was removed from the furnace and placed into the water-quenching device within 15 seconds. / Die volledig geaustenitiseerde toetsstuk is uit die oond verwyder en binne 15 sekondes in die waterblustoestel geplaas.

Two flats are ground along the test specimen length to a depth of 0.5 mm and 180° apart. / Twee plat kante word langs die toetsstuklengte tot 'n diepte van 0.5 mm en 180° uitmekaar geslyp.

If the hardness measurements at the same distances along the specimen length for: (i) a pair of opposing flats 180° apart differ at most by 5 HRC and (ii) for a second pair of opposing flats on the same specimen has a maximum spread of 3 HRC. / As die hardheidmetings op dieselfde afstande langs die monsterlengte vir: (i) 'n paar teenoorstaande plat kante 180° van mekaar verskil hoogstens met 5 HRC verskil en (ii) vir 'n tweede paar teenoorgestelde vlakke op dieselfde toetsstuk 'n maksimum verspreiding het van 3 HRC.

Flowing water at a temperature of 15 °C is used to perform the quenching of the test specimen end within the water-quenching device. / Vloeiende water by 'n temperatuur van 15 °C word gebruik om die bluswerk van die einde van die toetsstuk binne die waterblustoestel uit te voer.

If the hardness measurements at the same distances along the specimen length for: (i) a pair of opposing flats 180° apart differ at most by 5 HRC and (ii) for a second pair of opposing flats on the same specimen has a maximum spread of 5 HRC. / As die hardheidmetings op dieselfde afstande langs die monsterlengte vir: (i) 'n paar teenoorstaande plat kante 180° van mekaar verskil hoogstens met 5 HRC verskil en (ii) vir 'n tweede paar teenoorgestelde vlakke op dieselfde toetsstuk 'n maksimum verspreiding het van 5 HRC.